产品介绍：ECCtreme™ ECA是一种新型的全氟塑料，被设计用于最高300°C的高温场合，同时具有优越的电性能和耐化学性能。ECCtreme™ ECA可以通过正常的高温氟塑料加工设备在正常的操作速度下进行熔融加工，同时其具有聚四氟乙烯的物理性能、电性能和耐化学性能。
当ECCtreme™ ECA进过热才处理后，性能会得到进一步提升，例如更高的熔点、更高的熔体粘度、更好的抗应力开裂性能。这种效果为当树脂加热到280°C保温一段时间后产生的附生共结晶现象（Epitaxial co-crystallization,ECC)。
ECCtreme™ ECA 3000氟塑料独特的耐高温性能可以满足在石油天然气开采和地热发电行业中苛刻的高温环境对材料的要求。例如，可以用ECCtreme™ ECA生产潜油电泵(ESP)的电线和其它部件、油井测井电缆、输油管路高温伴热电缆；也可用于汽车内部高温环境下的氧传感器等。
ECA树脂的典型性质
| ASTM标准 | 单位 | ECCtreme™ ECA3000 | ECCtreme™ ECA3000(热处理7天) | |
| 热学性质 | ||||
| 熔点 | ASTM D4591 | °c | 320 | 325 |
| 灌在最高使用温度 | UL746B | °c | 300 | 300 |
| 熔融指数 | ASTMD1238 | g/10min | 5 | 2 |
| 机械性能 | ||||
| 拉伸强度 | ASTM D1708 | MPa(psi) | ||
| 23°C | 15(2,280) | 17(2,400) | ||
| 200°C | 8(1,130) | 10(1,500) | ||
| 300°C | 3(400) | 4(550) | ||
| 断裂伸长率 | ASTM D1708 | % | ||
| 23°C | 194 | 214 | ||
| 200°C | 319 | 453 | ||
| 300°C | 483 | 532 | ||
| 拉伸模量 | ASTM D1708 | MPa(psi) | ||
| 23°C | 522(75,700) | 610(88,400) | ||
| 200°C | 88(12,700) | 101(14,600) | ||
| 300°C | 14(2,000) | 21(3,100) | ||
| 耐折性 | ASTM D2176 | MIT | 14,000 | 53,000 |
| 硬度 | ASTM D2240 | shore D | D55 | D55 |
| 冲击理度，凹口-41°C | ASTM D256 | 不断 | 不断 | |
| 冲击强度，非凹口 175°C | ASTM D4812 | 不断 | 不断 | |
| 电学性能 | ||||
| 介电常数 | ASTM D150 | 100Hz | 2.09 | 2.21 |
| 牌号 | 形状 | MFR | 特征 | 成型法 | 典型用途 |
| 2000 | 颗粒 | 2 | 最高使用温度300°C， 耐应力开裂 | 传递成型，挤出成型 | 阀门、管件内衬，管材 |
| 3000 | 3 | 最高使用温度300°C， 耐应力开裂 | 挤出成型，注塑成型 | 油井测井电缆，管材 | |
| 4000 | 14 | 最高使用温度300°C， 耐应力开裂，高速线缆挤出 | 挤出成型，注塑成型 | 高温线缆，油井测井电缆 |
耐热性基准-连续最高使用温度， PTFE及PFA为260℃，FEP为200℃，ETFE为150℃，ECA为300℃，FFR为200℃~260℃
在极低温(-196°C)下，有5%的伸展度。同等条件下耐冲击特性，比其他树脂更佳。
几乎对所有的化学药品及溶剂都是稳定的。
固体绝缘材料中最小的介电常数、耗散因数、高频率、温度改变中呈现稳定。体积及表面电阻显示最大值。
在固体材料中具有最低的摩擦系数。加入玻璃纤维、碳素纤维、石墨、金属粉等无机的填充物后可改善其摩耗性，并可在严苛的环境下使用。
Teflon™极限氧指数（LOI）为95%以上的难燃性材料。燃烧热非常低，火灭时绝对不会扩大延烧而形成二度火源。Teflon™的极限氧指数（LOI）为30%，亦具有优良的阻燃性。
耐候性极佳，在室外长时间使用也不会氧化、引起表面污染、变色、品质变差等情形。
除具有添加物的产品外，Teflon™在化学上的惰性及纯度非常高。绝对不含有会引起污染的添加剂如増塑剂、稳定剂、润滑剂、抗氧剂。
纯的Teflon™由于其本身致密的质地和化学惰性，因此不会为微生物提供其生长所需的环境和氧份。
表面能为固体材料中最小，具有很好的不粘性，可做离型材料。
JIS规格
| 规格号码 | 规格名称 |
| JIS K6885 | SEAL用四氟乙烯树脂生料带(末加工Tape) |
| JIS K6886 | 四氟乙烯树脂产品的尺寸 |
| JIS K6887 | 四氟乙烯树脂 |
| JIS K6888 | 四氟乙烯树脂板 |
| JIS K6889 | 四氟乙烯树脂圆形棒 |
| JIS K6890 | 四氟乙烯树脂管 |
| JIS K6891 | 四氟乙烯树脂成型粉试验方法 |
| JIS K6892 | 四氟乙烯树脂糊状挤出成型粉试验方法 |
| JIS K6893 | 四氟乙烯树脂乳液试验方法 |
| JIS K6894 | 四氟乙烯树脂处理涂层(coating) |
| JIS K6895 | 四氟乙烯树脂产品的尺寸测量法 |
| JIS K6896 | 四氟乙烯树脂成型粉末 |
| JIS K6897 | 四氟乙烯树脂管 |
ASTM规格
| Teflon™ PTFE树脂 | ||||||
| 规格号码 | 规格名称 | |||||
| ASTM D1457 | PTFE Molding and Extrusion Materials | |||||
| ASTM D4894 | PTFE Granular Materials | |||||
| ASTM D4441 | Aqueous dispersions of PTFE | |||||
| ASTM D4895 | PTFE resin produced from dispersion(Fine Powder) | |||||
| ASTM D1710 | PTFE Fluoropolymer Rod | |||||
| ASTM D2571 | PTFE-backed pressure-sensitive electrical insulating tape | |||||
| ASTM D3293 | PTFE resin molded sheet | |||||
| ASTM D3294 | PTFE resin molded basic shapes | |||||
| ASTM D3295 | PTFE tubing | |||||
| ASTM D3308 | PTFE resin skived tape | |||||
| ASTM D1000 | Method of testing pressure-sensitive adhesive-coated tapes used for electrcal insulation | |||||
| ASTM D1895 | Test methods for apparent density, bulk factor and pourability of plastic materials | |||||
| ASTM D1675 | Method fo testing PTFE tubing | |||||
| ASTM D3297 | Practice for molding and machining tolerance for PTFE resin | |||||
| ASTM D902 | Method of testing flexible resin-coated glass fabrics and glass fabric tapes used for electrical insulation | |||||
| ASTM D3369 | PTFE fluoropolymer resin cast film | |||||
| ASTM F423 | PTFE plastic-lined ferrous metal pipe and fittings | |||||
| Teflon™ FEP 树脂 | ||||||
| 规格号码 | 规格名称 | |||||
| ASTM D2116 | FEP-Fluoroplymer Molding and Extrusion Materials | |||||
| ASTM D3296 | FEP-Fluoropolymer resin tubing | |||||
| ASTM D3368 | FEP-Fluoropolymer resin sheet and film | |||||
| ASTM F546 | FEP plastic-lined ferrous metal pipe and fittings | |||||
| Teflon™ PFA树脂 | ||||||
| 规格号码 | 规格名称 | |||||
| ASTM D3307 | PFA-Fluoropolymer Molding and Extrusion Materials | |||||
| ASTM F718 | PFA plastic-lined ferrous metal pipe and fittings | |||||
UL标准
| 规格号码 | 规格名称 |
| UL-1581 | 200°C Fixture Wire, TefLon™ FEP |
| UL-758 | 150°C and 200°C Appliance Wire； Tetlon™FEP and 250℃ Teflon™FEP PFA/PTFE |
CSA标准
| 规格号码 | 规格名称 |
| C-22.2No.210 | Appliance Wiring Material； 250℃ Teflon™ PTFE/PFA, 200°C Teflon™ FEP |
| C-22.2No.127 | Equipment Lead Wire； 250℃ Teflon™PTFE/PFA( 200°C Teflon™ FEP and 150°C Teflon™ FEP |
Military Specifications
| 规格号码 | 规格名称 |
| Mil-W-22729/1-12,20-31 | Wire, Electrical, Fluoropolymer insulated Extruded PTFE |
| Mil-W-22729/13,14,15 | Wire, Electrical, Fluoropolymer insulated FEP |
| Mil-C-27500C | Jaketed Materials; Teflon™ PFA |
氟化树脂的现有化学物质名称整理号码
| 名称 | 简称 |
现有化学 物质名称 整理思号码 |
| 四氟乙烯 | PTFE | 6-939 |
| 四氟乙烯共聚合物 | PFA | 6-944 |
| 四氟乙烯•六氟丙烯共聚物 | FEP | 6-946 |
•使用前请务必阅读产品安全说明书(MSDS)。如需要最新的MSDS,请联系您当地的销售代表。
•要加热至260°C时，一定要安装排气装置，使排气与换气充分进行，以避免吸入分解之气体。
注意事项
•若香烟附着氟塑料时，可能会有吸入分解气体的危险，因此在使用场所或工作场所一律禁烟，并且禁止携带香烟进入。
•使用后，应将衣服上附着的灰尘抖落，手脸洗净，不要让氟塑料附着于香烟上。
•本商品并无针对人体移植，或医疗用途设计生产。
•要废弃时，一定要依照废弃物处理及清扫的相关法律进行，绝对不可燃烧。
•不能使用于工作范围以外。
请填写您的问题，我们会尽快给您回复！
如有任何疑问，可以随时拨打我们的服务热线： 0755-82542786